A750

Application Segments

Aerospace

Melting Route

Airmelted

Product Description

BÖHLER A750 is an austentic, corrosion and heat-resistant chromium nickel steel, niobium stabilized and solution treated. It have been used typically for parts requiring good corrasion resistance and which will be subjected to elevated temperatures during fabrication or in service and for parts requiring oxidation resistance up to 1500 °F (816°C),
but usage is not limited to such applications. Compared to common 13% chromium steel, it offers higher corrosion resistance at lower strength and good weldability. No post-weld heat treatment required. The steel is resistant to atmospheric corrosion and the action of steam, water and acid as well as alkaline solutions. For optimum resistance, surfaces should be pickled or polished. Cold forming properties are very good. The steel is capable of taking a mirror finish.

Property Features

Niobium stabilized, austenitic chromium nickel steel which resists intergranular corrosion in the temperature range up to 400°C (752°F). No post-weld heat treatment required. The steel is resistant to atmospheric corrosion and the action of steam, water and acid as well as alkaline solutions. For optimum resistance, surfaces should be pickled. Cold forming properties are very good. The steel is capable of taking a mirror finish.

Technical Specifications

Material Numbers


1.4546 X5CrNiNb18-10 Z6CnNb1810 S34700


Standards


5646 S130 970 Pt.3

Chemical Composition

Chemical composition (average %)
max. 0.08 max. 1 max. 2 max. 0.04 max. 0.03 17 to 19 max. 0.75 9 to 12 max. 0.75 max. 1 10xC to 1.1

Available product shapes

Information on Long Products ) Presented data refer exclusively to long products. Please observe the detailed explanations at the end of the data sheet (pdf).

  • Long Products
  • Plates